The two concepts of slag blending ratio in cement and admixing quantity of slag are liable to be confused when producing cement with clinker powder and slag powder .

采用熟料粉、矿渣粉拌和水泥生产工艺，往往易混淆水泥中矿渣粉配比和矿渣掺入量这两个概念。

With the greater demand of sulfureted antimony slag for market, the slag was become more and more after the process of selecting and smelting mine, whereas, the most slag freely placed wasn't disposed and treated in some degree. Meanwhile, there were some sulphur and valuable metals in the slag.

随着市场对硫化锑矿石的需求量越来越大，选矿之后和冶炼后产生的矿渣也越来越多，大多数矿渣随处堆放未作处理和治理，另外矿渣中含有一定的硫磺和贵重金属资源。

Slag concrete can be equivalent to replace 20%~ 70% of cement, the fly ash, slag powder when the double-doped slag still be equivalent to replace 30% to 40% cement.

混凝土中矿渣粉可等量替代20%～70%水泥，在粉煤灰、矿渣粉双掺时矿渣粉依然可等量替代30%～40%水泥。

Water-quenched samples were prepared by re-melting blast furnace slag and then quenching it at different temperatures. The effects of forming process on the relationship between structure and cementitious reactivity of quenched slag were studied by XRD, DTA, TEM, SEM and EDX techniques in combination with mechanical property and alkali leaching tests.

采用重新熔融水淬的方法制备不同水淬矿渣样品，综合进行净浆强度实验和碱溶出实验研究，借助XRD，DTA，TEM，SEM和EDX等分析手段，研究了矿渣形成过程、形成结构和胶凝性能之间的关系，并在此基础上探讨了矿渣潜在胶凝活性的形成机理。

Using metallurgical slag Pangang development to produce 10 series over 20 kinds of slag building materials products, main products have slag gravel, slag sand,·, silicate block, gutter cover, color pavement bricks, ordinary silicon Salts cement, composite powders, brightener, high titanium proppant fracturing oil and commodity concrete.

公司利用攀钢冶金废渣开发生产出10大系列20多种矿渣建材产品，主要产品有矿渣碎石、矿渣砂、路沿石、硅酸盐砌块、水沟盖板、彩色路面砖、普通硅酸盐水泥、复合微粉、光亮剂、高钛石油压裂支撑剂和商品混凝土等。

Every road property of slag cement concrete was varied in slag content, as its content is 30%, the mechnical property and durability of concrete were higher than that of other slag content.

矿渣水泥砼的各项路用性能随矿渣掺量的变化不同，当矿渣掺量为30％时。砼的力学性能和耐磨性能均高于其他掺量的砼。

It is clear that this study can be referenced by engineering person to compute several parameters and modify the relative criterion, and the broad application of ground blast furnace slag to the engineering concrete can be guided by it.

由研究成果可以为磨细矿渣混凝土应用于路面工程中时确定工程设计参数提供依据及相关的规范设计提供参考，为磨细矿渣粉在工程中的大规模应用提供一定的理论依据，促进了大掺量磨细矿渣混凝土在实际工程中的大力开拓应用。

The experimental results show as follows: Slag could inhibit the cracking of concrete within the range of certain proportion. With the increase of slag proportion the self-shrinking of concrete increases, but the drying shrinkage of concrete decreases.

结果表明矿渣掺量在一定范围内时可抑制混凝土的开裂，混凝土的自收缩随矿渣掺量的增大而增大，干缩随矿渣掺量的增大而减小。

The experimental results show as follows: Slag could inhibit the cracking of concrete within the range of certain proportion. With the increase of slag proportion the selfshrinking of concrete increases, but the drying shrinkage of concrete decreases.

结果表明矿渣掺量在一定范围内时可抑制混凝土的开裂，混凝土的自收缩随矿渣掺量的增大而增大，干缩随矿渣掺量的增大而减小。

Many research achievement have been acquired mainly on the studies of activator, durability and setting time of alkali-activated slag cement and concrete.

碱矿渣水泥是用碱金属的碱性化合物激发矿渣形成的胶凝材料，以之为基础的碱矿渣混凝土具有高强、快硬、低水化热、耐久等优良性能。

Methods: Five patients with parkinsonism or dystonia were assigned to general anesthesia using an modified endotracheal tube.

本实验依照人体实验之相关规定进行，五位患有帕金森氏症或肌张力异常的病人接受神经立体定位手术。

If you can benefit from this book, it is our honour.

如果您能从本书获益，这将是我们的荣幸。