水泥

At the same W/C condition, ocean-sand (standard and non-standard) is mixed, non-standard ocean-sand shall have more compressive strength than standard ocean-sand about 10%, Add slag additament to motor test sample of ocean-sand mixing, bending strength shall be according to slag additament, but 40%~60% slag additament shall be quite obvious. Motor test sample of ocean-sand mixing shall be compared type Ⅰ cement with type Ⅱ cement, to make use of type Ⅱ cement to motor test sample of ocean-sand mixing shall have more compressive and bending strength about 10%, Rising of strength is best among non-standard sand mixing.

若添加炉石於海砂所拌和的水泥砂浆，其抗弯强度会随著炉石添加量的增加而增加，以40%~60%的炉石替代量为最佳；以第Ⅰ及第Ⅱ类型所拌和的海砂水泥砂浆试体做比较，依晚期强度而言，第Ⅱ类型水泥所拌和的试体，其抗压及抗弯强度比第Ⅰ类型水泥约高出10%左右，其中以非标准砂所拌和的试体强度上升最大。

The large and medium-sized cement enterprises in our country generally use high-quality bituminous coal and low quality coal can not been used.

随着优质资源的日益稀少，水泥工业逐渐向利用低质燃料的方向发展，但局限于当前的水泥生产工艺水平，能够适应水泥生产的煤种范围比较窄，一般我国水泥工业中的大中型企业多使用优质烟煤，劣质煤很难得到应用。

On the basis of the comprehensive study and analysis of the literatures concerning the mechanism and properties of CCWC, the substances that can react with anhydrate or hydration products and other supplementary ingredients were selected, and variety of experiments were conducted by means of cross experimental design. The effects of chemical composition and dosage of raw materials, curing condition, and chemical admixtures on waterproofing ability were tested and analyzed.

本文在对水泥基渗透结晶型防水材料的作用机理和应用性能分析研究基础上，选择能与水泥混凝土中未水化水泥及部分水化产物反应的活性物质和其它的辅助成分，利用正交设计方法，研究不同组分对涂料防水性能的影响，并详细分析了原料化学成分、掺量及养护条件等参数的变化对涂料渗透结晶性能的影响，研制成功了一种以硅酸盐水泥为基础的水泥基渗透结晶型防水涂料—GT防水涂料。

Micronucleus test results exhibited that significant differences in micronuclear rates were determined between 0.4 mL bone cement and 0.4 mL microsphere-coated bone cement groups and negative control group, but no significant difference was detected among other groups. This revealed that this microsphere-coated bone cement leaching liquor did not show significant cell heredity toxic effects. Nevertheless, microsphere-coated bone cement in the high concentration and high dosage groups exhibited low toxic effects, mainly showing increased hemolysis rate and micronuclear rate. Thus, it was necessary to control the dosage and concentration of microsphere-coated bone cement.

微核实验结果显示除0.4 mL骨水泥组和0.4 mL微球骨水泥组的微核率与阴性对照组差异有显著性意义，其余各组差异无显著性意义，说明该微球骨水泥的浸提液无明显细胞遗传毒性作用，但是高浓度和高剂量组的微球骨水泥仍有较低的毒性作用，主要表现为溶血率和微核率的提高，因此在应用时要适当控制微球骨水泥的剂量和浓度。

It is higher demand of slip casting engineering of imperious curtain of municipal refuse landfill , because its coarse grain and higher sweating rate when its concretion and its antacial poor stability of cement cumulates, its difficult to meet the design specification of antiseepage by the onefold cement slip casting.

城市垃圾卫生填埋场对防渗帷幕注浆的要求较高，单纯的水泥注浆，由于水泥颗粒较粗、水泥浆液凝固时的析水率较高、水泥固结体抗酸稳定性较差，很难满足设计对防渗的要求。采用粘土水泥固化浆液相关性能均能满足垃圾填埋场防渗帷幕的要求。

It is also revealed that the refractoriness of Portland cement and alumina cement are actually at the identical level, and refractoriness of castable with low cement content of Portland cement, substitution of alumina cement, will not cause worsening of refractoriness.

研究还发现硅酸盐水泥耐火度与矾土水泥耐火度实为同一水平，低水泥耐火浇注料中硅酸盐水泥替代矾土水泥不会造成浇注料耐火度的恶化。

Theoretical analysis on three series of cements, i. e. Portland cement, high alumina cement and sulpho-aluminous cement, shows that alkalinity of the pore fluid of the balanced hydration product of sulpho-aluminous cement is the lowest, and its strength and alkalinity can be adjusted further by the adjustment of its components.

目前硅酸盐水泥、铝酸盐水泥、硫铝酸盐水泥等三大系列水泥的理论分析表明：硫铝酸盐水泥系列水化产物平衡时的液相碱度是最低的，且经过改性还可以进一步改善其强度和碱度等综合性能。

A new type cement commonly apply closed-circuit circulatory system, that cement production not only rely on closed-circuit grinding system as well as the election system to elect the cement powder, but also the dust collection system to close down.

新型水泥制备普遍采用闭路循环系统，闭路水泥生产不仅要靠粉磨系统把水泥磨出来，靠选粉系统把水泥选出来，还要靠收尘系统把水泥收下来。

They used limestone of different quality and large-fluctuant-range waste stone in proportion and substituted a part of clay with clay stone to produce cement. And the physical performance of the produced Portland cement was improved greatly-28 d strength increased from 50.4MPa to 54.5MPa, and output of the rotary kiln increased. Moreover, the company also tried to use green shale as admixture to produce compound cement and successfully produced compound Portland cement with a little low early strength and a little higher 28d strength than slag Portland cement. And the cement cost decreased 19.59 yuan per ton.

将CaO含量波动范围较宽的废石与不同品位石灰石按比例搭配使用，将其粘土质特性的废石替代部分粘土生产；而且生产的硅酸盐水泥熟料物理性能有较大提高，28d强度由原来的50.4 MPa提高到54.5 MPa，窑产量也有一定的提高；此外，该公司还进行了将绿色页岩作混合材生产复合水泥的生产探索，成功生产出了早期强度略低，但28d强度略高于矿渣硅酸盐水泥的复合硅酸盐水泥，且使水泥生产成本降低19.59元/t。

Our main products are: computer automated rapid freezing and thawing of concrete tester, concrete carbonation chamber, concrete move Miriam, concrete to accelerate the conservation of boxes, concrete mixer, cement mortar conservation tank, cement rapid conservation boxes, cement paste mixer, cement glue sand mixer, cement mortar Tap Taiwan, the electric bending testing machine, making me boil marcescens, electric saws stone machine, sieve analysis of negative pressure device, Rutting Tester, Pavement Deflection Tester, rotating compaction test equipment etc..

公司主要产品有：微机全自动混凝土快速冻融试验仪、混凝土碳化试验箱、混凝土动弹仪、混凝土加速养护箱、混凝土搅拌机、水泥胶砂养护水槽、水泥快速养护箱、水泥净浆搅拌机、水泥胶砂搅拌机、水泥胶砂振实台、电动抗折试验机、雷氏沸煮箱、电动锯石机、负压筛析仪、车辙试验仪、路面弯沉试验仪、旋转压实仪等试验设备。