In order to increase the practical application of this waster water treating technology, in this text, we tried to improvement the feasible on economy and technology from preparation of photocatalysists, design of reactor and the influence of different reaction conditions etc.A P25 TiO2 film supported on UV light surface was prepared using sol-gel method at 200℃ calcinations temperature, and the photocatalyst has shown a good stability and performance for the photodegradation of orthocresol solution irradiated with UV light of 254nm, when reaction for 30min, the photodegradation still more then 85%.

为了更快地将这种处理技术用于大规模生产当中，本文以焦化废水中的邻甲酚作为目标污染物，试图从催化剂薄膜的制备、反应器的设计、反应条件的影响等各方面来深入研究TiO_2膜催化剂的催化降解作用以便促进提高其实际应用中的经济技术可行性。

Silica sol without ethanol was prepared with tetraethyl orthosilicate as precursor.

以硅酸乙酯为水解前驱体，制备了有机硅水溶胶体系。

While the molar ratio of WD-20 and tetraethyl orthosilicate was 0.2, the sol-fraction of the prepared nanocomposites was 6%,glass transition temperature was above 250 ℃ and the transmittance was more than 80% at the wavelength between 450 nm and 800 nm and the size of dispersed SiO2 phase was less than 100 nm.

当WD-20与四乙基原硅酸盐之比为0.2时，所制备的纳米复合材料的溶胶分数为6%、玻璃化转变温度为250 ℃以上、可见光透过率在80％以上、SiO2分散相尺寸小于100 nm。

Palmitic acid-silicon dioxide nano-composite phase change material was prepared by sol-gel process from tetraethyi orthosilicate and palmitic acid.

采用溶胶—凝胶法，以正硅酸乙酯和棕榈酸为主原料，制备了一种有机—无机纳米复合相变材料。

Nanu-SiO2 was syrtthesized though hydrolyzation-condensation of n- tetraethyl orthosilicate in organic solvent using sol-gel method.

西北工业大学理学院，西安710072摘要：采用溶胶一凝胶法，利用正硅酸乙酯在有机溶剂中的水解-缩合制备纳米SiO2。

Porous carbons were prepared with tetraethyl orthosilicate as the silica template and solube starch and β-cyclodextrin as carbon precursor by sol-gel method.

以正硅酸乙酯为模板硅源，β-环状糊精和可溶性淀粉分别为碳前驱体，运用溶胶-凝胶法制备了多孔炭材料。

The sol-gel solution was prepared by mixing ethyl orthosilicate, absolute alcohol and 0.1molL^(-1) HCl in a definite proportion, and adding an appropriate amount of silicotungstic acid as active material, strring for 30min and then standing for 24h at room temperature.

溶胶－凝胶溶液系将正硅酸乙酯、无水乙醇及0.1molL^(-1)盐酸按一定比例混合后加适量的硅钨酸作为活性物质，搅拌30min混匀后在室温放置24h配成。

Monolayer high anti-reflective coatings are coated by sol-gel method with tetraethyl orthosilicate and silicon oil(MW≈500) as precursor and ammonia as catalyst.

以正硅酸乙酯和硅油为前驱体，在碱性催化体系中制备出有机硅改性二氧化硅溶胶，采用提拉法获得了具备疏水性能的二氧化硅减反膜。

Hydroxyethyl cellulose and tetraethyl orthosilicate are chosen as the stuffs for the reaction, and HEC/SiO2 organic/inorganic hybrid are prepared by Sol-Gel process.

以羟乙基纤维素、正硅酸乙酯为原料，采用溶胶－凝胶技术合成了HEC/SiO2有机－无机杂化材料。

Samples prepared by sol-gel method have the largest OSC and suitable specific surface area.

采用溶胶—凝胶法制备的储氧材料老化前有较大的储氧量和合适的比表面。