ML/min,the end of reaction(pH=7).These precipitates were then peptized with peptizator HAc at 80 ℃ for 12 h. So a stable transparent colloidal sol was obtained.By using this sol,splinterless La2O3-Al2O3 membranes were prepared.

mL/min、反应终点(pH=7)，加入HAc作胶溶剂，于80 ℃恒温胶溶12 h，可制得稳定、透明的溶胶，用该溶胶可制得无开裂的La2O3-Al2O3膜。

Thixotropy of peptized concentrated aqueous pseudo-boehmite suspensions of SD and TY was performed with different methods including hysteresis loop and steady shear measurements.

采用经典的滞后环方法和恒剪切速率方法分别考察了山东工业拟薄水铝石和实验室自制拟薄水铝石胶溶所形成的浓水溶性悬浮体系的触变性。

Such a process includes the preparation of an initial stabilized peptized solution including a titanium precursor material, an organic solvent, an acid agent, the mixing of said initial solution with a large amount of water, the pH of the obtained intermediate solution being less then 3, subjecting said intermediate solution and its dispersion to a heat-treatment, the exchange of water by an organic solvent with low surface tension to obtain a final solution that is finally dispersed.

这样一种方法包括制备包含钛母体材料、有机溶剂、酸介质之开头的稳定化胶溶溶液，将此起始溶液同大量水混合，所得到中间溶液的pH小于3，使此中间溶液及其分散体系经受热处理，用低表面张力的有机溶剂更换水来获得末了加以分散的最终溶液。

The measurement of acid dispersion index indicates that the pseudo-boehmite powder canbe peptized completely. When n_H+/n_AlOOH·nH2O =0.097, the corresponding pH value is 3.4. The calculated potential barrier is 6.31 ×10~-18J according to DLVO model. The size of the colloidal particulates is around 5-10nm, being cross-link as is shown by TEM.

酸分散指数的测定表明当n_/n_(AlOOH·nH_2O)=0.097时，拟薄水铝石可以完全胶溶，稳定水溶胶的pH值为3.4；根据DLVO模型计算的位能势垒为6.31×10~(-18)J；TEM观察溶胶的胶粒为5-10nm，且部分粒子相互网联。

When I started coding, I had problems with the ASF file writer.

当我开始编码，我曾与ASF文件作家的问题。

I know that in one of the schools the boys have risen up in the classroom and enlisted in a mass.

如果你们也和他们一样，是集体自愿的话，你们的老师将是多么地光荣啊。