The results showed that when retrogressed by electrical current heating at 200 ℃ the tensile strength in re-aged 7A04 alloy extrusion bar of 60 mm in diameter reached 620-640 MPa and a uniform elongation appeared from central part to surface layer of the sample while the fracture time in test of resistance to stress corrosion under a load stress of 375MPa in 3%NaCl+0.5%H2O2 corrosion solution was greater than 30 d.
结果表明，直径60 mm的7A04铝合金棒材在200℃电流直接加热回归后再时效，从心部到表层的拉伸强度为620-640 MPa，延伸率均匀一致；在3%NaCl+0.5%H2O2水溶液介质中和375 MPa应力下的应力腐蚀断裂时间大于30d，而辐射式加热回归的为575 MPa，延伸率从心部至表层表现极不均匀，应力腐蚀断裂时间只有19 d。
-
The results showed that when retrogressed by electrical current heating at 200℃the tensile strength in re-aged 7A04 alloy extrusion bar of 60 mm in diameter reached 620- 640 MPa and a uniform elongation appeared from central part to surface layer of the sample while the fracture time in test of resistance to stress corrosion under a load stress of 375MPa in 3%NaCl+0.5%H_2O_2 corrosion sol...
结果表明，直径60 mm的7A04铝合金棒材在200℃电流直接加热回归后再时效，从心部到表层的拉伸强度为620-640 MPa，延伸率均匀一致；在3%NaCl+0.5%H_2O_2水溶液介质中和375 MPa应力下的应力腐蚀断裂时间大于30 d，而辐射式加热回归的为575 MPa，延伸率从心部至表层表现极不均匀，应力腐蚀断裂时间只有19 d。
-
Fluetubes and 4 super heater flues with stainless steel radiant type elements.
fluetubes和4个不锈钢超辐射式加热器烟道的元素。
- 更多网络解释与辐射式加热相关的网络解释 [注：此内容来源于网络，仅供参考]
-
panel heating：辐射式加热
panel doctor 主治医生 | panel heating 辐射式加热 | panel house 妓院
-
panel house：妓院
panel heating 辐射式加热 | panel house 妓院 | panel 面板
-
liquid-filled radiators：冲液式散热器
2.辐射式加热器radiant heaters | 3.冲液式散热器liquid-filled radiators | 4.风扇式加热器fan heaters
-
radiant heating：加热,辐射热供暖
radiant heater||辐射式供暖器 | radiant heating||加热,辐射热供暖 | radiant heating system||辐射式供暖系统
-
radiant heating system：辐射式供暖系统
radiant heater 辐射式供暖器 | radiant heating system 辐射式供暖系统 | radiant heating 加热
-
radiant heating element：辐射加热组件
radiant heating 辐射式供暖 | radiant heating element 辐射加热组件 | radiant intensity 辐射强度