The experimental results suggest that the bonding strength of nickel-lanthanum electrodeposits is higher than that of bright nickel.

实验结果，镍－镧镀层与基体的结合强度高于亮镍镀层与基体的结合强度。

In order to further improve the properties of tin electrodeposits, a multifunctional sulfate tin plating additive was developed.

为进一步提高镀锡层的性能，研制出一种多功能硫酸盐镀锡添加剂。

It has been discovered that the phosphorus and iron in the electrodeposits show cooperative effect, which has been studied in the view of quantum chemistry firstly.

发现了镀层中Fe与P存在协同效应，并且首次采用量子化学的观点从分子水平上对铁磷的协同效应进行了研究。

The surface morphologyand composition of bulk electrodeposits were characterized by means of thescanning electron microscopy.

通过扫描电子显微镜对镀层的微观形貌和成分进行了表征。

XRD results show that there is amorphous Mg-Ni phase and microcrystalline Mg phase in the electrodeposits.

XRD显示沉积层中含有非晶态Mg-Ni相和微晶态Mg相。

The being used plating technologies are not satisfied because that pinholes and cracks appear in electrodeposits due to hydrogen absorption.

但现在的电沉积工艺因吸氢严重致使镀层含有大量的气孔和裂纹，不能满足要求。

The result shows that the corrosion resistance of nano-composite electrodeposits prepared under pulse current condition is obviously better than that under o...

结果表明，在脉冲条件下所制备纳米复合电镀层的耐蚀性明显优于其它电镀层，其原因是电镀层中复合有适量的纳米ZrO2颗粒以及脉冲电沉积工艺本身所致。

Formula and plating parameters were optimized by Hull Cell test, properties of electrolyte and tin electrodeposits were also tested.

通过赫尔槽试验优选出最佳镀液配方和工艺条件，并对镀液、镀层性能进行了测试。

The effect of the concentrations of main salts and the process conditions on the compositions, and the morphologies of Sn-Ag-Cu alloy electrodeposits were investigated by X-ray fluorescence and scanning electron microscopy.

采用X射线荧光光谱仪和扫描电子显微镜研究了镀液中主盐浓度和电镀工艺条件对镀层的组成和形貌的影响。

A Ni-ZrO_2 nano-composite were prepared by electrodeposition.The corrosion resistance of the Ni-ZrO_2 nano-composite electrodeposits in 10%HCl and 10%H_2SO_4 solutions respectively was studied by massloss measurement.SEM was used to observe the morphology of various electrodeposits after corrosion test,and the relevant corrosion mechanism was discussed.

采用电镀工艺制备了纯镍电镀层和Ni-ZrO2纳米复合电镀层，对纯镍电镀层和Ni-ZrO2纳米复合电镀层分别在10%HCl和10%H2SO4溶液中的耐蚀性进行了对比研究，用SEM对各种电镀层腐蚀后的表面形貌进行了观察。

But in the course of internationalization, they meet with misunderstanding and puzzlement.

许多企业已经意识到了这一点，但在国际化的进程中，仍存在一些误区与困惑。

Inorder toaccomplish this goal as quickly as possible, we'll beteamingup with anexperienced group of modelers, skinners, and animatorswhosenames willbe announced in the coming weeks.

为了尽快实现这个目标，我们在未来数周内将公布与一些有经验的模型、皮肤、动画制作小组合作。